After vacuum gas quenching D2 tool steel, even if the surface hardness reaches HRC 58-60, the microstructure may still contain 15% - 25% Retained Austenite. 

Since austenite is a soft and unstable phase, it leads to two major technical issues:

1. Hardness Limitation:Prevents the material from reaching its maximum potential of 62+ HRC.

2. Dimensional Instability:Over time, retained austenite slowly transforms into martensite, causing microscopic volume expansion—a fatal flaw for high-precision molds.

Timing and Methodology of Sub-zero Treatment

To ensure complete transformation, sub-zero treatment should be performed immediately after the quenching cycle when the parts reach room temperature: Process Temperature:Typically ranging from -70°C to -190°C. A vacuum cryogenic chamber using liquid nitrogen circulation is the most effective equipment.

Operational Flow:

Post-Quench:Once the workpiece cools below 50°C (cool to the touch).

Cryogenic Soaking:Gradually decrease the temperature to the target and hold for 2-4 hours.

Immediate Tempering:After cryogenic treatment, the parts must immediately undergo vacuum tempering to relieve stresses and stabilize the newly formed martensite.

Effects:

Typically gains an additional 1-3 HRC, significantly increasing tool wear resistance.Eliminates the risk of deformation during service, extending the lifespan of precision cold work dies.

Click to read the article on [Vacuum Gas Quenching Furnace Application in D2 Tool Steel], or visit our website [SIMUWU] to learn more.